SSRT of 10-4 FeCrAl in LBE and Pb to Characterize Liquid Metal Embrittlement Effects

Sammanfattning

In this work the susceptibility of Fe-10Cr-4Al steel to liquid metal embitterment (LME)in low oxygen environment was investigated. slow strain rate testing (SSRT) wereconducted on 10-4 FeCrAl steel in a stagnant lead from 340-480◦C, lead-bismutheutectic (LBE) from 140-450◦C and lead-bismuth mixture at 375◦C with increasingbismuth content from 0.1wt%-40wt%. The results showed that in the stagnant leadenvironment the FeCrAl steel showed no sign of LME with all samples being subjectedto around 25% strain before final break. In LBE the samples were affected by LMEespecially at 350-400◦C. The total elongation to failure reduced in LBE from 25%to 13.1% and a ductility trough from 190-400◦C was observed. In the lead-bismuthmixture there was a reduction in ductility at 5wt% going from 25% to 20% totalelongation, at 15wt% going from 20% to 16% total elongation and at 30wt% going from16% to 13% total elongation.